1.3243, HS6-5-2-5, AISI M41 - high speed steel

Hot-rolled and forged bars, forgings in high speed steel HS6-5-2-5, 1.3243, AISI M41, UNS T11341 acc. to ISO 4957, DIN 17350.

16 Types Of Steel Defects:Pay Attention When Choosing

Some high-speed steel components do not meet the GB/T9943-2008 High-speed Tool Steel standard, especially for the high or low content of carbon. W6Mo5Cr4V2Co5 belongs to the HSS-E type, because the carbon content is lower than the standard lower limit. B hss steel w6mo5cr4v2co5#214;HLER High Speed Steelskh51:aisi m2:1.3343:hs6-5-2 w6mo5cr4v2 skh55:aisi m35:1.3243:hs6-5-2-5:w6mo5cr4v2co5:skh59:aisi m42:1.3247:hs2-10-1-8:w2mo9cr4vco8

B hss steel w6mo5cr4v2co5#214;HLER High Speed Steel

skh51:aisi m2:1.3343:hs6-5-2 w6mo5cr4v2 skh55:aisi m35:1.3243:hs6-5-2-5:w6mo5cr4v2co5:skh59:aisi m42:1.3247:hs2-10-1-8:w2mo9cr4vco8 China Carbon Steel, Alloy Steel, HSS Hand and Machine China Carbon Steel, Alloy Steel, HSS Hand and Machine Taps, Find details about China Hand Tap, Machine Tap from Carbon Steel, Alloy Steel, HSS Hand and Machine Taps -

China HSS Round Push Broaches - China Hss Round Broach

B. W6Mo5Cr4V2Co5 (GB), M35( ASTM), 1.3243(DIN), SKH55(JIS) chemical composition:C 0.93, Si 0.38, Mn 0.35, P0.030, S0.030, Cr 4.10, W 6.30, Mo 4.80 V 1.85, Co 5.00 main application:It is often used for making blades with high-speed and great cutting difficulty as it's good abrasive resistance China High Speed Steel M35 with 5% Cobalt - China 1.3243 China High Speed Steel M35 with 5% Cobalt, Find details about China 1.3243, W6mo5cr4V2co5 from High Speed Steel M35 with 5% Cobalt - Dalian Jingtai Industry Trade Co., Ltd.

Customized High Speed Steel M35 for Circle Saw Blades

High Speed Steel M35 for Circle Saw Blades. W6Mo5Cr4V2Co5 M35 1.3243 SKH55 0.91 0.32 0.35 0.018 0.005 4.1 6.3 4.98 1.95 4.8 HSS M35 Feature: hss steel w6mo5cr4v2co5#183; all-round applicability hss steel w6mo5cr4v2co5#183; good machine-ability HIGH SPEED STEEL AND TUNGSTEN CARBIDE ANNULAR HIGH SPEED STEEL Performance FOR HSS cobalt 5%-M35 HSS CODE:W6Mo5Cr4V2Co5 (M35) Chemical compositons(%):C Si Mn W Mo Cr V Co 0.88-0.96 0.20-0.60 0.2-0.40 6.0-6.70 4.70-5.20 3.80-4.50 1.70-2.00 4.5-5.0 International Code:ASTM:M35(A600) UNS:JIS:SKH55 DIN:S6-5-2-5 BS:NF:HS6-5-2-5 ROCT:P6M5K5 ISO:HS6-5-2-5 ChinaM35 Density Annealed(g/cm):8.11 Heat

HSS COBALT 5-M35

Translate this pageHSS5-M35. HSSW6Mo5Cr4V2Co5M35 C Si Mn W Mo Cr V Co . 0.88-0.96 0.20-0.60 0.2-0.40 6.0-6.70 4.70-5.20 3.80-4.50 1.70-2.00 4.5-5.0 High Speed Steel Bar (M35/SKH55)(id:3538932). Buy China HIGH SPEED STEEL M35/SKH55 1. Formula:W6Mo5Cr4V2Co5 2. Size:2 to 200mm 3. Application:Cutting tools under high temperature. Anneal temperature:840-860 Relief annealing temperature:720-760 Hardening temperature:1200-1235 Hardening medium:Salt bath under 600, aslo use oil cooling or air cooling Normal temper temperation:540-560

High speed steel High speed steel, 440C VG10 Stainless

M35 W6Mo5Cr4V2Co5 SKH55 1.3243 High Speed Steel. M35 cobalt-containing high-speed steel, through appropriate heat treatment, can obtain high hardness (HRC67 ~ 70), high red hardness (625 hss steel w6mo5cr4v2co5#176; C 4 hours, HRC 63 ~ 65) and high wear resistance, toughness and bending strength are not lower than ordinary High-speed steel can overcome early damage such as mold edge collapse and cracking. High speed steel High speed steel, 440C VG10 Stainless M35 W6Mo5Cr4V2Co5 SKH55 1.3243 High Speed Steel. M35 cobalt-containing high-speed steel, through appropriate heat treatment, can obtain high hardness (HRC67 ~ 70), high red hardness (625 hss steel w6mo5cr4v2co5#176; C 4 hours, HRC 63 ~ 65) and high wear resistance, toughness and bending strength are not lower than ordinary High-speed steel can overcome early damage such as mold edge collapse and cracking.

Hss drill bits, twist drill bits, 4241, 4341, 9341, 6542

The HSS (High Speed Steel) materials used in these HSS twist drill bits have many grades. In China, the common HSS grades to make twist drill bits are 4241, 4341, 9341, 6542, M35. Except M35, the numbers in these grade names represent the approximate percentages of tungsten, molybdenum, chromium and vanadium in the HSS material. M35 Tool Steel SKH55 HS6-5-2-5 1.3243 High Speed Tempering Of HSS M35 Tool Steel Tempering temperature / :540-564 After tempering hardness HRC or higher:64 Application of Sae M35 tool Steel HSS M35 high speed steel is the main feature containing Co general cutting tool steel, quenching hardness is 1200-1240 c. Main use cutter, broach, end milling cutter. For manufacturing strong

M35 Tool Steel SKH55 HS6-5-2-5 |1.3243 HSS China supplier

M35 Tool Steel SKH55 HS6-5-2-5 1.3243 High Speed Steel. AISI M35 Tool Steel is high cobalt high speed steel. And M35 HSS containing cobalt high speed steel compared with low cost and easy processing, through the proper heat treatment, can get high hardness (67-70HRC), high hot hardness (625 for 4 hours and 63 ~ 65HRC), whats more, high wear resistance, toughness and bending hss steel w6mo5cr4v2co5 - Arc en cielhss steel w6mo5cr4v2co5. 1.3243, HS6-5-2-5, AISI M41 - high speed steel. M35 High Speed Steel Round Bar 1.3243 / SKH55 HSSM35 High speed steel round bar is supplied in the annealed and machineable condition. Re annealing will only be necessary if the steel has been hot worked, forged, or hardened by the toolmaker.